Vertical type sensor

ABSTRACT

The present invention provides a vertical type sensor, including a substrate; a first electrode formed on the substrate; a sensing layer formed on the first electrode layer and reactive to a target substance, wherein the first electrode layer is interposed between the substrate and the sensing layer; and a second electrode layer formed on the sensing layer and having a plurality of openings, wherein the sensing layer is interposed between the first electrode layer and the second electrode layer, and the target substance contacts the sensing layer via the plurality of openings. The vertical type sensor of the present invention provides instant, sensitive and rapid detection.

CROSS-REFERENCES TO RELATED APPLICATIONS

This application claims under 35 U.S.C. §119(a) the benefit of TaiwaneseApplication No. 99134543, filed Oct. 11, 2010, the entire contents ofwhich is incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to sensors, and more particularly, to avertical type sensor.

2. Description of Related Art

In the field of medical therapy, it is a trend to develop a sensor, suchas a sensor for detecting biological molecules. Particularly, in orderto achieve instant measurement and monitor chronic diseases, it is themajor trend to develop a detecting method which has high sensitivity,instant and precise detection, and reproducibility.

U.S. Patent Application Publication No. 20020092342 discloses a gassensor, as shown in FIG. 10, including a back electrode 71, a SiCsemiconductor layer 72 formed on the back electrode 71, an aluminumnitride layer 73 formed on the SiC semiconductor layer 72, and a gateelectrode 74 formed on the aluminum nitride layer 73. The gate electrode74 is a porous catalytically active metal electrode for forming anionized product after the reaction of the target gas and the gateelectrode 74, and then the ionized product diffuses to an interface ofthe aluminum nitride layer 73 and the gate electrode 74, so as to changepotential distribution and voltage shift, thereby achieving thedetection. Similarly, U.S. Patent Application Publication No.20020020853 and U.S. Patent Application Publication No. 20090113992disclose the usage of catalytically active metals.

In addition, H. T. Wang et al., APPLIED PHYSICS LETTERS 86, 243503(2005) and F. Razi et al., Sensors and Actuators B: Chemical 146 (2010)53-60 disclose a horizontal type sensors. In H. T. Wang et al., the zincoxide pillar is formed by vapor deposition, and then the position of theelectrode is defined. The gas concentration is identified by thehorizontal type sensor based on the change of resistance; however, thestability of such horizontal type sensor is not so satisfied due to thesignificant variation of pillar distribution. In the horizontal typesensor of F. Razi et al., the substrate is made of porous p-typedsilicon, and palladium is deposited on the silicon substrate, whereinhydrogen is trapped by palladium, and the porous silicon substrate isused for carrying palladium rather than detecting the target gas.Further, the metal electrodes, made of different materials, of thehorizontal type sensor are identified by photolithography, such that thefabrication is complicated.

Therefore, there is a need to develop a sensor with high sensitivity,instant measurement, easy-to-read signal and reproducibility.

SUMMARY OF THE INVENTION

The present invention provides a vertical type sensor including asubstrate; a first electrode layer formed on the substrate; a sensinglayer formed on the first electrode layer, wherein the first electrodeis interposed between the substrate and the sensing layer, and thesensing layer is made of a material reactive to a target substance orhas a portion reactive to a target substance; and a second electrodelayer formed on the sensing layer, wherein the sensing layer isinterposed between the first electrode layer and the second electrodelayer, the second electrode layer has a plurality of openings, and thetarget substance contacts the sensing layer via the openings of thesecond electrode layer.

In an aspect of the present invention, the sensing layer has a firstporous structure with openings upwards corresponding to the openings ofthe second electrode layer.

In an aspect of the present invention, the vertical type sensor of thepresent invention further includes a semiconductor layer inactive to thetarget substance, and the semiconductor layer is disposed on the top orbottom of the sensing layer. In addition, the sensing layer has openingsupwards corresponding to the openings of the second electrode layer. Thesemiconductor layer can also have a second porous structure withopenings upwards corresponding to the openings of the second electrodelayer.

In an aspect of the present invention, the sensing layer includes aplurality of sensing sublayers. For example, a first, second and thirdsensing sublayers are sequentially formed on the first electrode layer.In addition, in one embodiment, the first and second sensing sublayersrespectively have a third porous structure with openings alignedupwards, and the third sensing sublayer has a fourth porous structureformed randomly. Alternatively, the first sensing sublayer has a thirdporous structure with openings upwards, and the second and third sensingsublayers have openings upwards corresponding to the openings of thesecond electrode layer.

The present invention further provides a method for forming a verticaltype sensor. The method includes the steps of providing a substrate witha surface formed with a first electrode layer thereon; forming a sensinglayer on the first electrode layer, wherein the sensing layer isreactive to a target substance; applying a plurality of firstnanoparticles on the sensing layer in a manner that a portion of a topsurface of the sensing layer is exposed from the plurality of firstnanoparticles; forming a second electrode layer on the exposed portionof the top surface of the sensing layer, wherein the sensing layer isinterposed between the first electrode layer and the second electrodelayer; and removing the plurality of first nanoparticles to form aplurality of openings in the second electrode layer for exposing thesensing layer, wherein the target substance contacts the sensing layervia the plurality of openings.

In one embodiment of the present invention, the method further includesthe step of removing a part of the sensing layer for forming a pluralityof openings in the sensing layer upwards corresponding to the openingsof the second electrode layer.

In an aspect of the present invention, the method further includes thestep of forming an inert semiconductor layer on the first electrodelayer before forming the sensing layer. Alternatively, the methodfurther includes the step of forming an inert semiconductor layer on thefirst electrode layer before applying the plurality of firstnanoparticles. In addition, after removing the plurality of firstnanoparticles, the method further includes the step of removing acertain portion of the sensing layer and the inert semiconductor layerby using the second electrode layer as a mask, such that the sensinglayer has openings upwards corresponding to the openings of the secondelectrode layer, and the inert semiconductor layer has a second porousstructure with openings upwards corresponding to the openings of thesecond electrode layer.

In the method of the present invention, the sensing layer can haveopenings formed randomly.

In an aspect of the present invention, the sensing layer includes aplurality of sensing sublayers. For example, a first, second and thirdsensing sublayers are sequentially formed on the first electrode layer.In addition, in one embodiment, the first and second sensing sublayersrespectively have a third porous structure with openings alignedupwards, and the third sensing sublayer has a fourth porous structureformed randomly. Alternatively, the first sensing sublayer has a thirdporous structure with openings upwards, and the second and third sensingsublayers have openings upwards corresponding to the openings of thesecond electrode layer. The third porous structure is formed by thesteps of applying a plurality of nanoparticles on the first electrodelayer to expose a portion of the first electrode layer; forming amaterial reactive to the target substance on the portion of the firstelectrode layer; and removing the plurality of nanoparticles to form thethird porous structure. The openings of the second and the third sensingsublayers are formed by using the second electrode layer as a mask andremoving a part of the second and the third sensing sublayers afterremoving the plurality of nanoparticles.

The present invention further provides a method for forming a verticaltype sensor, includes the steps of providing a substrate having asurface formed with a first electrode layer; forming a first sensingsublayer on the first electrode layer; applying a plurality ofnanoparticles on the first sensing sublayer to expose a portion of thefirst sensing sublayer; forming sequentially a second sensing sublayer,a third sensing sublayer and a second electrode layer on the portion ofthe first sensing sublayer; removing the nanoparticles to form openingsof the second electrode layer for exposing the first sensing sublayer,wherein the target substance contacts the first, the second and thethird sensing sublayers.

The present invention further provides a detecting method, including thesteps of applying a bias voltage to the first electrode layer and thesecond electrode layer of the vertical type sensor of the presentinvention to form current; providing the target substance to contact thesensing layer of the vertical type sensor; and measuring a change ofelectrical property of the vertical type sensor.

The present invention further provides a detecting system, including avertical type sensor of the present invention; a voltage supply deviceelectrically connected to the first electrode layer and the secondelectrode layer of the vertical type sensor for providing a bias voltageto the vertical type sensor; and a detecting device electricallyconnected to the vertical type sensor for measuring a change ofelectrical property of the vertical type sensor.

In a preferred embodiment, the change of electrical property is a changeof current.

The vertical type sensor of the present invention has instantmeasurement, and high sensitivity. Furthermore, the vertical type sensorof the present invention provides a change of current for detection,such that expensive detecting equipments are not needed so as todecrease cost and be used for large-scale screening.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A to FIG. 1D are schematic views showing the method for formingthe vertical type sensor according to the present invention;

FIG. 2 is a schematic view showing a cross-section of another verticaltype sensor according to the present invention;

FIG. 3A to FIG. 3D are schematic views showing a vertical type sensorhaving an inert semiconductor layer according to the present invention;

FIG. 4 is a schematic view showing a vertical type sensor according tothe present invention;

FIG. 5A to FIG. 5C are schematic views showing a vertical type sensorand a method for forming the vertical type sensor according to thepresent invention;

FIG. 6A to FIG. 6B′ are schematic views showing a vertical type sensorand a method for forming the vertical type sensor according to thepresent invention, wherein FIG. 6A′ and FIG. 6B′ provides the methoddifferent from that shown in FIG. 6A and FIG. 6B, respectively;

FIG. 7 is a schematic view showing a detecting system having a verticaltype sensor of the present invention;

FIG. 8A and FIG. 8B are diagrams showing the vertical type sensor of thepresent invention having an aluminum electrode with a plurality ofopenings, and the vertical type sensor of the present invention having asensing layer with a first porous structure, respectively, by scanningelectron microscopy;

FIG. 9A to FIG. 9C are images showing a change of current of a verticaltype sensor according to the present invention; and

FIG. 10 is a schematic view showing a gas sensor disclosed in U.S.Patent Application Publication No. 20020092342.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The detailed description of the present invention is illustrated by thefollowing specific examples. Persons skilled in the art can conceive theother advantages and effects of the present invention based on thedisclosure contained in the specification of the present invention.

In the present invention, the structure, scale and size shown indrawings are provided for persons skilled in the art to understand thedisclosure of the present invention rather than limiting the practice ofthe present invention. The present invention covers any modifications,variations and adjustments of the structures which achieve effects andpurposes of the present invention. In addition, the terms, such as “on”,“top”, “bottom”, and “one”, herein are used for illustrating the presentinvention rather than limiting the scope of the present invention.

The First Embodiment

Referring to FIG. 1A to FIG. 1D, a method for forming a vertical typesensor of the present invention is shown.

As shown in FIG. 1A, a first electrode layer 11, such as indium tinoxide, is formed on a surface of a substrate 10, and a sensing layer 12is formed on a surface of the first electrode layer 11. The sensinglayer 12 is made of a material reactive to a target substance or thesensing layer 12 has a portion reactive to a target substance. Theportion of the sensing layer 12 is made of an inert material such assemiconductor material, conductive material or insulating material andthe portion (a receptor, for example) of the sensing layer 12 is abinding or a contact to the inert material. For example, the sensinglayer 12 may have a probe group for binding or contacting the inertmaterial. The probe group is one or more selected from the groupconsisting of —OH, —CHO, —COOH, —SO₃H, —CN, —NH₂, —SH, —COSH, —COOR anda halide. In addition, the probe group may be a biological moleculeselected from the group consisting of a nucleic acid, an antibody, anantigen, a polysaccharide, a protein, an amino acid, and an enzyme.

For example, the probe group is biotin. Biotin has specific binding toits substrate such as avidin, and thus the vertical type sensor of thepresent invention is capable of specifically detecting the presence ofavidin in the target substance.

The sensing layer can be made of a semiconductor material, which is oneor more selected from the group consisting of In—Ga—Zn—O (IGZO), zincoxide (ZnO_(x)), titanium dioxide and indium oxide. The aboveillustrated probe group may bind to or contact the semiconductormaterial, conductive material or insulating material.

In one embodiment, the sensing layer may be, but not limited to, anorganic polymer semiconductor, such as

Usually, the organic polymer semiconductor can be formed as the sensinglayer by spin coating. Alternatively, the sensing layer may be formedfrom other materials by deposition.

As shown in FIG. 1B, a plurality of nanoparticles 13 having a diameterof 200 nm are applied on the sensing layer 12 by immersing. Thenanoparicles may be polystyrene beads. Preferably, the nanoparticles 13are applied as a single layer to expose a portion f the top surface ofthe sensing layer 12.

As shown in FIG. 1C, a second electrode layer 14, such as aluminum, isformed on the exposed surface of the sensing layer 12 by sputtering,such that the sensing layer 12 is interposed between the first electrodelayer 11 and the second electrode layer 14.

As shown in FIG. 1D, the nanoparticles 13 are removed by using anadhesive tape, such that openings 141 are formed in the second electrodelayer 14 to expose the sensing layer 12, such that the target substanceis allowed to contact the sensing layer 12.

According to the above illustrated method, the vertical type sensor ofthe present invention includes a substrate 10; a first electrode layer11 formed on the substrate 10; a sensing layer 12 formed on the firstelectrode layer 11, wherein the first electrode layer 11 is interposedbetween the substrate 10 and the sensing layer 12, and the sensing layer12 is made of a material reactive to a target substance or the sensinglayer 12 has a portion reactive to a target substance; and a secondelectrode layer 14 formed on the sensing layer 12 such that the sensinglayer is interposed between the first electrode layer 11 and the secondelectrode layer 14, and the second electrode layer 14 has a plurality ofopenings 141 for the target substance to contact the sensing layer 12.

The Second Embodiment

Referring to FIG. 2, another vertical type sensor of the presentinvention is illustrated.

As shown in FIG. 2, the present embodiment is similar to the firstembodiment except that after removing the nanoparticles 13, a portion ofthe sensing layer 12 is removed by using the second electrode layer 14as a mask and using oxygen plasma, such that a first porous structure 15is formed and has openings upwards corresponding to the openings 141 ofthe second electrode layer 14.

Hence, the sensing layer 12 of the vertical type sensor has a firstporous structure 15 with openings upwards corresponding to the openings141 of the second electrode layer 14.

Referring to FIG. 3A to FIG. 3F, another vertical type sensor of thepresent invention is shown.

As shown in FIG. 3A to FIG. 3D, the present embodiment is similar to thefirst embodiment except an additional inert semiconductor layer 16.

As shown in FIG. 3A, before forming the sensing layer 12, an inertsemiconductor layer 16 is formed on the first electrode layer 11. Thesemiconductor layer 16 of the vertical type sensor is disposed at thebottom surface of the sensing layer 12 and inactive to the targetsubstance.

As shown in FIG. 3B, before the nanoparticles are applied as illustratedin FIG. 1B, the inert semiconductor layer 16 is formed on the sensinglayer 12. Thus, the inert semiconductor layer 16 is formed on the topsurface of the sensing layer 12. As shown in FIG. 3C and FIG. 3D, afterthe process shown in FIGS. 3A and 3B that forming the second electrodelayer 14 is formed and the nanoparticles 13 are removed, is performed, aportion of the sensing layer 12 and the inert semiconductor layer 16 areremoved by using the second electrode layer 14 as a mask, such that thesensing layer 12 has openings upwards corresponding to the openings 141of the second electrode layer 14, similar to the first porous structure15, and the inert semiconductor layer 16 has a second porous structure17 with openings upwards corresponding to the openings 141 of the secondelectrode layer 14.

The Fourth Embodiment

Referring to FIG. 4, another vertical type sensor of the presentinvention is shown. The vertical type sensor of the present embodimentis similar to that of FIG. 1D except that the sensing layer 12 hasopenings 15′ formed randomly. The openings 15′ are formed by the waysimilar to the above illustration except that the polystyrene beads arestacked for several layers on the first electrode layer 1, the materialreactive to the target substance is filled in the space between thepolystyrene beads, and after removing the polystyrene beads, the sensinglayer 12 has the openings 15′ formed randomly. Taiwan Patent No.98108545 discloses the formation of the porous sensing layer which isincorporated herein as reference. In addition, the porous sensing layercan be formed by electric spinning.

The Fifth Embodiment

Referring to FIG. 5A to FIG. 5C, another vertical type sensor of thepresent invention is shown.

In the present embodiment, the sensing layer of the vertical type sensorincludes a plurality of sensing sublayers. For example, the sensinglayer 12 includes a first sensing sublayer 121, a second sensingsublayer 122, and a third sublayer 123 sequentially formed on the firstelectrode layer. The first sensing sublayer 121 and the second sensingsublayer 122 have a third porous structure 18 with openings alignedupwards, and the third sensing sublayer 123 has a fourth porousstructure 19 formed randomly.

As shown in FIG. 5A, the third porous structure 18 is formed by thesteps of applying a single layer 13′ of nanoparticles on the firstelectrode layer 11 in a manner that a portion of the surface of thefirst electrode layer 11 is exposed from the single layer 13′ ofnanoparticles; forming the material or the portion reactive to thetarget substance on the exposed surface of the first electrode layer 11,wherein the materials of the first sensing sublayer 121 and the secondsensing sublayer 122 are different; and removing the single layer 13′ ofnanoparticles, so as to form a third porous structure 18.

As shown in FIG. 5B and FIG. 5C, the fourth porous structure 19 isformed by the way illustrated in the fourth embodiment, and then asecond electrode layer 14 is formed, so as to obtain the vertical typesensor of the present invention.

The Sixth Embodiment

Referring to FIG. 6A to FIG. 6B, another vertical type sensor of thepresent invention is illustrated.

In the present embodiment, the sensing layer of the vertical type sensorincludes a first sensing sublayer 121, a second sensing sublayer 122 anda third sublayer 123, wherein the first sensing sublayer 121 has a thirdporous structure 18 with openings upwards, and the second sensingsublayer 122 and the third sensing sublayer 123 have openings upwardscorresponding to the openings 141 of the second electrode layer 14.

As shown in FIG. 6A and FIG. 6B, the first sensing sublayer 121 isformed by the way illustrated in the fifth embodiment. Before applyingthe nanoparticles 13, the second sensing sublayer 122 and the thirdsensing sublayer 123 are formed, and after forming the second electrodelayer 14 and removing the nanoparticles, a portion of the second sensingsublayer 122 and that of the third sensing sublayer 123 are removed byusing the second electrode layer 14 as a mask.

As shown in FIG. 6A′ and FIG. 6B′, the present invention providesanother method for forming a second sensing sublayer 122 and a thirdsensing sublayer 123. Before forming the second electrode layer 14 asshown in FIG. 1B, the second sensing sublayer 122 and the third sensingsublayer 123 are sequentially formed on the exposed portion of the topsurface of the first sensing sublayer 121. Then, the nanoparticles areremoved, such that the second electrode layer 14 has openings forexposing the first sensing sublayer 121. Thus, the target substancecontacts the first sensing sublayer 121, the second sensing sublayer 122and the third sublayer 123.

In the vertical type sensor having a first sensing sublayer 121, asecond sensing sublayer 122 and a third sublayer 123, it is preferableto have at least one sensing sublayer reactive to the target substance.

The Seventh Embodiment

Referring to FIG. 7, a detecting system including the vertical typesensor of the present invention is shown.

As shown in FIG. 7, the detecting system includes a vertical type sensor40 of the present invention; a voltage supply device 41 electricallyconnected to a first electrode layer 402 and a second electrode layer402 of the vertical type sensor 40 for providing a bias voltage to thevertical type sensor 40; and a detecting device 42 electricallyconnected to the vertical type sensor 40 for measuring a change ofelectrical property of the vertical type sensor 40.

When a vertical type sensor with a plurality of sensing sublayers isused in a detecting system, and one of the sensing sublayers iselectrically conductive, the voltage supply device can be electricallyconnected (by a conductive wire, for example) to such sensing sublayer.Similarly, while in detecting, a bias voltage may be applied to thesensing sublayer, and then the change of electrical property of thevertical type sensor is measured. In addition, the vertical type sensorof the present invention may further include a third electrode layer 403embedded in the sensing layer. Preferably, the third electrode layer 403has a gate structure, and is formed by patternization process or usingnanoparticles as illustrated in the above. The voltage supply device mayalso be electrically connected to the third electrode layer 403 toprovide more detection data.

Test

In the vertical type sensor formed in the second embodiment of thepresent invention, the first electrode layer is made of indium tinoxide, the sensing layer is made of P3HT(poly(3-hexylthiophene-2,5-diyl)), which is an organic semiconductormaterial reactive to ammonia and has a thickness of 60 nm, and thesecond electrode layer is made of aluminum and has a thickness of 40 nmFIG. 8A shows that the aluminum electrode has a plurality of openings,and FIG. 8B shows the sensing layer of the vertical type sensor of thepresent invention has a first porous structure.

In the control group, the vertical type sensor is formed by the waysimilar to that illustrated in the first embodiment of the presentinvention except that no nanoparticles are used, such that the secondelectrode layer of the vertical type sensor of the control group has noopenings.

In the test, the vertical type sensor of the present invention and thevertical type sensor of the control group are respectively placed innitrogen environment, voltage is applied to the vertical type sensor ofthe present invention and the vertical type sensor of the control group,then ammonia is introduced into the nitrogen environment, and therelease of the gas is controlled.

FIG. 9A is a diagram showing the current change of the vertical typesensor of the control group while introducing 5 ppm of ammonia, whereinthere is some, but not significant, current change at time 270 to 370second and at time 430 to 520 second. In contrast, FIG. 9B shows thatthe vertical type sensor of the present invention has significantcurrent change while introducing 1.72 ppm and 5 ppm of ammonia. Inaddition, while introducing 0.5 ppm of ammonia, the vertical type sensorof the present invention also has significant current change, as shownin FIG. 9C. Accordingly, the vertical type sensor is much more sensitivedue to having a second electrode layer with openings or a sensing layerhaving a corresponding first porous structure. Especially, afterrepetitive use, the vertical type sensor of the present invention stillhas satisfactory sensitivity. In addition, the sensitivity of thedetection is reduced to about 0.05 ppm.

In the present invention, the second electrode layer with openings isformed by using nanoparticles rather than photolithography process. Themethod of the present invention provides a controllable porous structure(such as the openings of the second electrode layer or the first andsecond porous structures). Hence, the method of the present invention issimple and provides a sensor with high reproducibility. In addition, thevertical type sensor of the present invention has high sensitivity,instant measurement, fast operation, and no need to be applied with highvoltage.

Furthermore, the porous structure with openings upwards, especiallyaligned with the openings of the second electrode layer, has an uniformstructure, and thus has faster recovery in response to the reversiblesensing layer or prove group.

The invention has been described using exemplary preferred embodiments.However, it is to be understood that the scope of the invention is notlimited to the disclosed arrangements. The scope of the claims,therefore, should be accorded the broadest interpretation, so as toencompass all such modifications and similar arrangements.

The invention claimed is:
 1. A vertical type sensor, comprising: asubstrate; a first electrode layer formed on the substrate; a sensinglayer formed on the first electrode layer and reactive to a targetsubstance, wherein the first electrode layer is interposed between thesubstrate and the sensing layer; and a second electrode layer formed onthe sensing layer and layer having a plurality of openings so as toexpose the sensing layer via the openings, wherein the sensing layer isinterposed between the first electrode layer and the second electrodelayer, and the target substance contacts the sensing layer via theplurality of openings.
 2. The vertical type sensor of claim 1, whereinthe sensing layer has openings formed randomly or a first porousstructure.
 3. The vertical type sensor of claim 2, wherein the firstporous structure of the sensing layer has openings upwards correspondingto the openings of the second electrode layer.
 4. The vertical typesensor of claim 1, further comprising a semiconductor layer being inertto the target substance and disposed on the top or bottom of the sensinglayer.
 5. The vertical type sensor of claim 4, wherein the sensing layerhas openings upwards corresponding to the openings of the secondelectrode layer.
 6. The vertical type sensor of claim 5, wherein thesemiconductor layer has a second porous structure with openings upwardscorresponding to the openings of the second electrode layer.
 7. Thevertical type sensor of claim 1, wherein the sensing layer comprises aplurality of sensing sublayers.
 8. The vertical type sensor of claim 7,wherein the sensing layer comprises a first, a second and a thirdsensing sublayers sequentially formed on the first electrode layer. 9.The vertical type sensor of claim 8, wherein the first and the secondsensing sublayers respectively have a third porous structure withopenings aligned upwards, and the third sensing sublayer has a fourthporous structure formed randomly.
 10. The vertical type sensor of claim8, wherein the first sensing sublayer has a third porous structure withopenings upwards, and the second and the third sensing sublayersrespectively have openings upwards corresponding to the openings of thesecond electrode layer.
 11. The vertical type sensor of claim 1, whereinthe sensing layer has a portion reactive to the target substance, andthe portion of the sensing layer is a probe group.
 12. The vertical typesensor of claim 11, wherein the probe group comprises one or moreselected from the group consisting of —OH, —CHO, —COON, —SO₃H, —CN,—NH₂, —SH, —COSH, —COOR and a halide.
 13. The vertical type sensor ofclaim 11, wherein the probe group is a biological molecule selected fromthe group consisting of a nucleic acid, an antibody, an antigen, apolysaccharide, a protein, an amino acid, and an enzyme.
 14. Thevertical type sensor of claim 1, further comprising a third electrodelayer embedded in the sensing layer.
 15. A detecting system, comprising:a vertical type sensor of claim 1; a voltage supply device electricallyconnected to the first electrode layer and the second electrode layer ofthe vertical type sensor for providing a bias voltage to the verticaltype sensor; and a detecting device electrically connected to thevertical type sensor for measuring a change of electrical property ofthe vertical type sensor.
 16. A method for forming a vertical typesensor, comprising the steps of: providing a substrate having a surfaceformed with a first electrode layer thereon; forming a sensing layer onthe first electrode layer, wherein the sensing layer is reactive to atarget substance; applying a plurality of first nanoparticles on thesensing layer in a manner that a portion of a top surface of the sensinglayer is exposed from the plurality of first nanoparticles; forming asecond electrode layer on the portion of the top surface of the sensinglayer wherein the sensing layer is interposed between the firstelectrode layer and the second electrode layer; and removing theplurality of first nanoparticles and forming a plurality of openings inthe second electrode layer so as to expose the sensing layer via theopenings, wherein the target substance contacts the sensing layer viathe plurality of openings.
 17. The method of claim 16, wherein thesensing layer has a portion reactive to the target substance, and theportion of the sensing layer is a probe group, wherein the probe groupcomprises one or more selected from the group consisting of —OH, —CHO,—COON, —SO₃H, —CN, —NH₂, —SH, —COSH, —COOR and a halide, or the probegroup is a biological molecule selected from the group consisting of anucleic acid, an antibody, an antigen, a polysaccharide, a protein, anamino acid, and an enzyme.
 18. The method of claim 16, wherein thesensing layer is made of a semiconductor material which is one or moremetal oxides selected from the group consisting of zinc oxide, titaniumdioxide, and indium oxide.
 19. The method of claim 16, furthercomprising the step of removing a part of the sensing layer for forminga plurality of openings in the sensing layer upwards corresponding tothe openings of the second electrode layer.